A method of preparing a precursor for a composite having wet strength of 2 to 50 kgf/mm and a mean surface void diameter of 0.01 to 2 mu m by molding a solution of a rigid polymer having a concentration of 1 to 1.3 times the optical anisotropy lower limit solution concentration C2, thereafter…